To reduce tool Build-Up and minimize the cost of tool wear during mass production, a combined theoretical and practical analysis approach is employed. This approach comprehensively examines the processing conditions, including processing efficiency, cooling methods, and material properties. It aims to address the issue of aluminum adhesion caused by aluminum melting, allowing for tool reuse and thus lowering tool consumption costs.

With the rapid development of China’s automotive industry, especially in the booming new energy vehicle sector, lightweighting has become a core topic. The key to lightweighting is changing traditional materials. Aluminum alloys, with their high strength and low weight, are essential for achieving vehicle lightweighting. The complex geometric shapes of automotive parts and the increasing proportion of die-cast aluminum alloy parts in vehicles have led to a growing demand for CNC machining of die-cast parts.

CNC machining of aluminum alloy automotive parts requires high efficiency, stable continuous production, and decreasing costs, necessitating more detailed control and planning of the entire production process.

How to Treat Tool Build-Up in Aluminum Alloy Cutting Processes Using Chemical Methods? 1

Tool Build-Up

Aluminum’s inherent property of low melting point causes it to become “sticky” during cutting. Due to this characteristic and inadequate cooling in actual conditions, the heat generated by friction during the microscopic cutting process cannot be released in time or effectively. This results in aluminum melting and adhering to the tool’s cutting edges and chip flutes. Upon cooling, the aluminum solidifies and sticks to the tool, forming build-up. This phenomenon, commonly referred to in the industry as “easy tool sticking,” leads to tool failure.

Tools are consumables in CNC machining processes and represent a significant cost component. Generally, cutting tools for aluminum alloys need to be sharper, with chip flutes specially polished and coated with aluminum-specific coatings to improve chip removal efficiency. The automotive industry’s push for high efficiency increases feed rates and cutting speeds, which raises the heat generated during cutting and the risk of aluminum melting and sticking to the tool, thereby increasing costs due to tool failure from build-up.

With environmental regulations, minimal quantity lubrication (MQL) is widely used as a cutting fluid alternative in aluminum alloy CNC machining. However, the low melting point of aluminum exacerbates the reduced cooling effect of MQL, further promoting build-up. Tools that fail due to sticking account for about 40% of conventional tool failures. Traditional methods of dealing with build-up, such as tapping or striking, rarely restore tools for reuse. Thus, a new solution is proposed.

Treatment Measures

The new solution involves the following steps:

  1. Remove the tool with build-up.
  2. Obtain solid NaOH, dilute it with water, and place it in a ceramic container.
  3. Once diluted into NaOH solution, immerse the tool with aluminum build-up in the solution. Ensure that the build-up areas are fully submerged and maintain immersion for 2 hours, or adjust based on practical conditions. Table 1 compares traditional and new treatment methods.
Traditional Treatment New Solution
Tools with aluminum build-up are discarded directly, leading to significant production costs Immersion liquid can remove aluminum from complex and irregular shapes
Physical methods like tapping and striking damage the polished surface, leading to tool discard or reduced cutting efficiency Short treatment time and simple operation
Short treatment time and simple operation Easy-to-obtain treatment materials with low cost

 Build-Up

Chemical Principles

Using A1Si7Mg material commonly found in automotive parts as an example, where A1 content is approximately 93.5%, Si content is 6.5%, and Mg content is 0.25%. Both Al and Si react with NaOH solution. Immersion in NaOH solution removes the primary A1 component from the tool. The principle involves the reaction between metal and NaOH, producing bubbles (H?), which eventually causes the adhered aluminum to detach.

Chemical reaction equations are as follows:

  1. Si reacts with NaOH: Si + 2NaOH + H?O → Na?SiO? + 2H?↑
  2. Al reacts with NaOH: 2Al + 2NaOH + 2H?O → 2NaAlO? + 3H?↑

The final result is the removal of aluminum, making the tool reusable.

Experimental Validation for Reducing Build-up

The theoretical method was tested using a tap. Taps are valuable tools in aluminum alloy machining, requiring a longer lifespan and featuring complex geometric shapes. Once aluminum adhesion occurs, physical removal is nearly impossible, making this test more significant and representative.

Due to high heat generated during machining and possible inadequate cooling, aluminum melts instantly and adheres to the flutes rendering the tap unusable due to damaged threads.

The test involved immersing the tap with aluminum build-up in NaOH solution.

The test conclusion: The tap, after complete immersion in NaOH, showed that the build-up had completely detached. Residual aluminum slag was found in the test container. The treated tap was used for further machining, and the workpiece threads met the required specifications. The tap was successfully restored for reuse.

How to Treat Tool Build-Up in Aluminum Alloy Cutting Processes Using Chemical Methods? 2

Conclusion

The automotive parts industry, characterized by mass production, requires extensive cutting validation during the initial equipment and tool design phase. Common issues such as build-up during validation due to parameter mismatches, equipment adjustments, and operator experience can significantly increase trial costs and production cycles. This method effectively addresses build-up issues, greatly reducing tool costs and processing time, extending tool life, and substantially lowering production costs.

4 September, 2024

Perfect

Leave a Reply

Your email address will not be published. Required fields are marked *

粉嫩国产一区二区三区在线| 在线视频三区日本精品| 亚洲国产中文字幕在线观看| 精品亚洲香蕉久久综合网| 国产精品色热综合在线| 日韩国产欧美中文字幕| 成人免费高清在线一区二区| 熟女乱一区二区三区四区| 激情少妇一区二区三区| 99久久国产精品亚洲| 国产又长又粗又爽免费视频| 日韩欧美一区二区不卡视频| 日韩精品一区二区一牛| 精品久久少妇激情视频| 亚洲av熟女国产一区二区三区站| 国产一区二区三区精品免费| 日韩一级一片内射视频4k| av在线免费观看一区二区三区| 伊人网免费在线观看高清版| 国产黄色高清内射熟女视频| 四十女人口红哪个色好看| 国产亚洲不卡一区二区| 精品国产亚洲av成人一区| 大香蕉伊人一区二区三区| 国产精品免费视频久久| 国产成人综合亚洲欧美日韩| 免费大片黄在线观看日本| 高清在线精品一区二区| 日韩欧美亚洲综合在线| 色一欲一性一乱—区二区三区| 国产亚洲精品岁国产微拍精品| 国产一区二区不卡在线视频| 国产中文字幕一二三区| 久久国产精品熟女一区二区三区| 粗暴蹂躏中文一区二区三区| 国产一级一片内射视频在线| 国产精品欧美一区二区三区不卡| 国产精品午夜一区二区三区| 九九久久精品久久久精品| 亚洲第一区二区三区女厕偷拍| 国产日韩中文视频一区|