{"id":1845,"date":"2019-05-22T02:48:24","date_gmt":"2019-05-22T02:48:24","guid":{"rendered":"http:\/\/www.meetyoucarbide.com\/single-post-application-of-woodworking-tungsten-carbide-cutting-tools\/"},"modified":"2020-05-04T13:12:02","modified_gmt":"2020-05-04T13:12:02","slug":"application-of-woodworking-tungsten-carbide-cutting-tools","status":"publish","type":"post","link":"https:\/\/www.meetyoucarbide.com\/tr\/agac-isleme-tungsten-karbur-kesme-aletleri-uygulamasi\/","title":{"rendered":"A\u011fa\u00e7 \u0130\u015fleme Tungsten Karb\u00fcr Kesme Aletleri Uygulamas\u0131"},"content":{"rendered":"
\n
\n
\u0130\u015fleme, \u00fcretim verimlili\u011fini, i\u015fleme maliyetlerini ve enerji t\u00fcketimini do\u011frudan etkileyen ah\u015fap end\u00fcstrisindeki en temel, en geni\u015f ve en \u00f6nemli s\u00fcre\u00e7lerden biridir. A\u011fa\u00e7 end\u00fcstrisi teknolojisinin ilerlemesi ile birlikte, \u00e7e\u015fitli ah\u015fap kompozit malzemeler, kontrplak, ah\u015fap, bambu glulam, \u00f6zellikle melamin emdirilmi\u015f ka\u011f\u0131t kontrplak, PVC kontrplak, Al 2 O3 takviyeli kontrplak ve di\u011fer malzemeler giderek daha fazla kullan\u0131lmaktad\u0131r. Mobilya, d\u00f6\u015feme, \u00e7at\u0131 panelleri ve m\u00fchendislik ah\u015fap par\u00e7alar\u0131 i\u00e7in. Bu malzemelerin kesilmesi zordur, basit kesme i\u015flemleri, geleneksel tak\u0131m konstr\u00fcksiyonu ve ortak tak\u0131m malzemelerinin elde edilmesi zor veya imkans\u0131zd\u0131r. Buna ek olarak, ah\u015fap end\u00fcstrisi teknolojisinin geli\u015fimi ile, suni tahta \u00fcretim ekipmanlar\u0131, \u00fcretim ekipmanlar\u0131, mobilya \u00fcretim ekipmanlar\u0131, vb. Y\u00fcksek derecede otomasyon, tam i\u015flevsellik, h\u0131zl\u0131 besleme ve y\u00fcksek \u00fcretim verimlili\u011fi y\u00f6n\u00fcnde hareket etmektedir. Teknolojideki her iki geli\u015fme de kesici tak\u0131m malzemelerinin ve \u00fcretim teknolojisinin geli\u015ftirilmesini desteklemi\u015ftir. Kesicinin normal kesim ger\u00e7ekle\u015ftirip ger\u00e7ekle\u015ftiremeyece\u011fi, kesim kalitesi iyi veya k\u00f6t\u00fcd\u00fcr ve dayan\u0131kl\u0131l\u0131k derecesi kesici kesim par\u00e7as\u0131n\u0131n malzemesi ile yak\u0131ndan ili\u015fkilidir. Kesme i\u015flemindeki \u00e7e\u015fitli fiziksel olaylar, \u00f6zellikle aletin a\u015f\u0131nmas\u0131 ve alet malzemesinin do\u011fas\u0131 b\u00fcy\u00fck \u00f6nem ta\u015f\u0131maktad\u0131r. Makine tak\u0131m\u0131na izin verildi\u011finde, tak\u0131m\u0131n verimlili\u011fi esas olarak malzemenin kendisinin yapabilece\u011fi kesme performans\u0131na ba\u011fl\u0131d\u0131r. A\u011fa\u00e7 i\u015fleme aletleri i\u00e7in gereklilikler, y\u00fcksek h\u0131z ve darbe ko\u015fullar\u0131nda kesme aletinin keskinli\u011fini uzun s\u00fcre korumakt\u0131r. Bu nedenle, ah\u015fap i\u015fleme aletinin malzemesi gerekli sertlik ve a\u015f\u0131nma direncine, yeterli mukavemet ve toklu\u011fa ve belirli bir i\u015f\u00e7ili\u011fe (kaynak, \u0131s\u0131l i\u015flem, kesme ve ta\u015flama gibi) sahip olmal\u0131d\u0131r.<\/div>\n

\"\"<\/p>\n

1. Karb\u00fcr ara\u00e7 malzemesi<\/h2>\n
\u00c7imentolu karb\u00fcr, ba\u011flay\u0131c\u0131 olarak Co, Ni, vb. \u0130le sinterlenmi\u015f olduk\u00e7a sert, refrakter metal karb\u00fcrden (WC, TiC) yap\u0131lm\u0131\u015f toz metalurji \u00fcr\u00fcn\u00fcd\u00fcr. Performans\u0131 esas olarak metal karb\u00fcr\u00fcn tipine, performans\u0131na, miktar\u0131na, par\u00e7ac\u0131k boyutuna ve ba\u011flay\u0131c\u0131 miktar\u0131na ba\u011fl\u0131d\u0131r. Sert ala\u015f\u0131m\u0131n sertli\u011fi HRC74 ~ 81.5'tir ve ba\u011flay\u0131c\u0131 olarak sertli\u011fi azal\u0131r<\/div>\n

\"\"<\/p>\n

i\u00e7erik artar. Semente karb\u00fcrdeki y\u00fcksek s\u0131cakl\u0131ktaki karb\u00fcr i\u00e7eri\u011fi, y\u00fcksek h\u0131z \u00e7eli\u011finden daha fazlad\u0131r, bu nedenle iyi termoplastikli\u011fe sahiptir ve 800-1000 \u00b0 C'ye kadar kesme s\u0131cakl\u0131klar\u0131na dayanabilir. Y\u00fcksek h\u0131zl\u0131 \u00e7eli\u011fin oda s\u0131cakl\u0131\u011f\u0131 sertli\u011fi 600 \u00b0 C'de a\u015f\u0131l\u0131r ve karbon \u00e7eli\u011finin oda s\u0131cakl\u0131\u011f\u0131 sertli\u011fini 1000 \u00b0 C'de a\u015far. Ah\u015fap ve ah\u015fap kompozitler i\u00e7in kesme aletleri, ba\u011flay\u0131c\u0131 olarak metal kobaltl\u0131 (Co) YG \u00e7imentolu karb\u00fcrleri ve sert faz olarak tungsten karb\u00fcr\u00fc (WC) kullan\u0131r. Son y\u0131llarda \u00e7e\u015fitli yeni kesici tak\u0131m malzemeleri ortaya \u00e7\u0131km\u0131\u015f olsa da, ah\u015fap esasl\u0131 panel end\u00fcstrisinde ve ah\u015fap i\u015fleme end\u00fcstrisinde otomasyonun geli\u015fmesiyle birlikte, a\u015f\u0131nmaya dayan\u0131kl\u0131 malzemeler olan sert al\u00fcminyum ala\u015f\u0131mlar\u0131 ana ah\u015fap i\u015fleri haline gelmi\u015ftir. tak\u0131m malzemeleri ve uzun bir s\u00fcre gelecek. \u0130\u00e7 k\u0131s\u0131m hala ah\u015fap kesici tak\u0131m malzemesinde \u00f6nemli bir yer tutacakt\u0131r. Semente karb\u00fcr k\u0131r\u0131lgan bir malzeme oldu\u011fundan, b\u00fck\u00fclme mukavemeti s\u0131radan y\u00fcksek h\u0131zl\u0131 \u00e7eli\u011fin yakla\u015f\u0131k 1\/4 ila 1\/2'sidir, darbe toklu\u011fu s\u0131radan y\u00fcksek h\u0131zl\u0131 \u00e7eli\u011fin yakla\u015f\u0131k 1\/30 ila 1\/4'\u00fc ve kesme kenar\u0131d\u0131r y\u00fcksek h\u0131z \u00e7eli\u011fi gibi parlat\u0131lamaz. Bu kadar keskin, karb\u00fcr kesici tak\u0131m malzemelerinin kesme performans\u0131n\u0131 daha da iyile\u015ftirmek ve iyile\u015ftirmek i\u00e7in yeni malzeme haz\u0131rlama tekniklerini ara\u015ft\u0131rmak ve geli\u015ftirmek gerekir.<\/div>\n

2 Karb\u00fcr kesici tak\u0131m malzeme ara\u015ft\u0131rma ve uygulama durumu<\/h2>\n
Karb\u00fcr kesici tak\u0131m malzemelerinin a\u015f\u0131nma direnci ve toklu\u011fu kolayca dikkate al\u0131nmad\u0131\u011f\u0131ndan, kullan\u0131c\u0131lar yaln\u0131zca belirli i\u015fleme nesnelerine ve i\u015fleme ko\u015fullar\u0131na g\u00f6re bir\u00e7ok karb\u00fcr kalitesi aras\u0131ndan uygun tak\u0131m malzemelerini se\u00e7ebilirler. Bu, \u00e7imentolu karb\u00fcr tak\u0131mlar\u0131n se\u00e7imine ve y\u00f6netimine rahats\u0131zl\u0131k getirir. Karb\u00fcr kesici tak\u0131m malzemelerinin kapsaml\u0131 kesme performans\u0131n\u0131 daha da art\u0131rmak i\u00e7in, mevcut ara\u015ft\u0131rma noktalar\u0131 genellikle a\u015fa\u011f\u0131daki y\u00f6nlere odaklanmaktad\u0131r.<\/div>\n

2.1 Tah\u0131l \u0130yile\u015ftirme<\/h3>\n
Sert faz\u0131n tane boyutunu d\u00fczelterek, taneler aras\u0131ndaki y\u00fczey alan\u0131n\u0131 art\u0131rarak ve taneler aras\u0131ndaki ba\u011flanma kuvvetini artt\u0131rarak, karb\u00fcr kesici tak\u0131m malzemesinin mukavemeti ve a\u015f\u0131nma direnci geli\u015ftirilebilir. WC'nin tane b\u00fcy\u00fckl\u00fc\u011f\u00fc mikron alt\u0131 \u00f6l\u00e7e\u011fin alt\u0131na d\u00fc\u015ft\u00fc\u011f\u00fcnde, malzemenin sertli\u011fi, toklu\u011fu, mukavemeti ve a\u015f\u0131nma direnci artt\u0131r\u0131labilir ve tam yo\u011funla\u015ft\u0131rma i\u00e7in gereken s\u0131cakl\u0131k da azalt\u0131labilir. S\u0131radan \u00e7imentolu karb\u00fcr\u00fcn tane b\u00fcy\u00fckl\u00fc\u011f\u00fc yakla\u015f\u0131k 3 ~ 5\u03bcm, ince taneli \u00e7imentolu karb\u00fcr\u00fcn tane b\u00fcy\u00fckl\u00fc\u011f\u00fc 1 ~ 1.5\u03bcm'dir ve ultra ince taneli \u00e7imentolu karb\u00fcr\u00fcn tane boyutu 0.5\u03bcm veya daha az\u0131na ula\u015fabilir. Ayn\u0131 bile\u015fime sahip s\u0131radan sert ala\u015f\u0131mlarla kar\u015f\u0131la\u015ft\u0131r\u0131ld\u0131\u011f\u0131nda, ultra ince taneli karb\u00fcrler sertli\u011fi 2HRA'dan daha fazla art\u0131rabilir ve e\u011filme mukavemeti 600 ~ 800MPa kadar artt\u0131r\u0131labilir. Ultra ince taneli karb\u00fcr giderek daha fazla kullan\u0131lmaktad\u0131r.<\/div>\n

2.2 Y\u00fczey, Genel Is\u0131l \u0130\u015flem ve D\u00f6ng\u00fcsel Is\u0131l \u0130\u015flem<\/h3>\n
\u0130yi sertlik ile sert ala\u015f\u0131m\u0131n y\u00fczeyindeki nitr\u00fcrleme, borlama, vb. \u0130\u015flemesi, y\u00fczey a\u015f\u0131nma direncini etkili bir \u015fekilde art\u0131rabilir. \u0130yi a\u015f\u0131nma direnci ancak zay\u0131f toklu\u011fa sahip sert ala\u015f\u0131mlar\u0131n genel \u0131s\u0131l i\u015flemi, malzemedeki ba\u011flay\u0131c\u0131 faz\u0131n bile\u015fimini ve yap\u0131s\u0131n\u0131 de\u011fi\u015ftirebilir ve WC sert faz\u0131n\u0131n biti\u015fikli\u011fini azaltabilir, b\u00f6ylece sert ala\u015f\u0131m\u0131n mukavemetini ve sertli\u011fini geli\u015ftirebilir. Tane s\u0131n\u0131rlar\u0131 aras\u0131ndaki stresi hafifletmek veya ortadan kald\u0131rmak i\u00e7in d\u00f6ng\u00fcsel bir \u0131s\u0131l i\u015flemin kullan\u0131lmas\u0131, sert ala\u015f\u0131m malzemesinin genel performans\u0131n\u0131 kapsaml\u0131 bir \u015fekilde geli\u015ftirebilir.<\/div>\n

2.3 Nadir metaller ekleme<\/h3>\n
\u00c7imentolu karb\u00fcr malzemelere TaC, NbC ve di\u011fer nadir metal karb\u00fcrlerin eklenmesi, katk\u0131 maddelerinin, sert faz yap\u0131s\u0131n\u0131 daha da g\u00fc\u00e7lendiren ve ayn\u0131 zamanda sert faz\u0131 bask\u0131layan karma\u015f\u0131k bir kat\u0131 \u00e7\u00f6zelti yap\u0131s\u0131 olu\u015fturmak i\u00e7in mevcut sert faz WC ile birle\u015fmesine izin verir. Tah\u0131l b\u00fcy\u00fcmesi, organizasyonun homojenli\u011fini ve di\u011fer etkilerini artt\u0131rmak, \u00e7imentolu karb\u00fcr\u00fcn genel performans\u0131n\u0131 b\u00fcy\u00fck \u00f6l\u00e7\u00fcde art\u0131racakt\u0131r. Ta (Nb) C'li bu tip semente karb\u00fcr ISO standard\u0131 P, K ve M karb\u00fcr kalitelerine eklenir.<\/div>\n

2.4 Nadir toprak elementleri ekleme<\/h3>\n
Semente karb\u00fcr malzemeye tantal gibi az miktarda nadir toprak elementinin eklenmesi, malzemenin toklu\u011funu ve e\u011filme mukavemetini etkili bir \u015fekilde art\u0131rabilir ve a\u015f\u0131nma direnci de geli\u015ftirilir. Bunun nedeni, nadir toprak elementinin sert faz\u0131 ve ba\u011flay\u0131c\u0131 faz\u0131n\u0131 g\u00fc\u00e7lendirebilmesi, tane s\u0131n\u0131r\u0131n\u0131 safla\u015ft\u0131rabilmesi ve karb\u00fcr kat\u0131 \u00e7\u00f6zeltisinin ba\u011flay\u0131c\u0131 faz\u0131na \u0131slanabilirli\u011fini geli\u015ftirebilmesidir. Nadir toprak elementleri i\u00e7eren karb\u00fcr ala\u015f\u0131mlar\u0131 kaba i\u015fleme i\u00e7in en uygundur ve \u00f6zellikle ah\u015fap ve ah\u015fap kompozit malzemelerin kesilmesi ve i\u015flenmesi i\u00e7in uygundur. \u00c7in'in nadir toprak kaynaklar\u0131 bol ve bu t\u00fcr karb\u00fcr kesme tak\u0131mlar\u0131n\u0131n geni\u015f uygulama beklentileri olacakt\u0131r. \u015eu anda, karb\u00fcr kesici tak\u0131m malzemeleri iki y\u00f6nde geli\u015fmektedir. Bir yandan, genel ama\u00e7l\u0131 markalar\u0131n uygulanabilir y\u00fczeyi gittik\u00e7e geni\u015fliyor ve \u00e7ok y\u00f6nl\u00fcl\u00fck g\u00fc\u00e7leniyor; \u00d6te yandan, \u00f6zel ama\u00e7l\u0131 markalar giderek daha fazla hedefleniyor ve daha uyumlu hale geliyor. Kesme verimlili\u011fini artt\u0131rmak amac\u0131yla i\u015flenen malzemenin do\u011fas\u0131 ve kesme ko\u015fullar\u0131.<\/div>\n

3. Kaplamal\u0131 karb\u00fcr<\/h2>\n
Sert, sert bir karb\u00fcr alt tabaka \u00fczerinde, CVD (Kimyasal Buhar Biriktirme), PVD (Fiziksel Buhar Biriktirme), PVCD (Plazma Geli\u015ftirilmi\u015f Kimyasal Buhar Biriktirme), HVOF (Y\u00fcksek H\u0131zl\u0131 Termal Kaplama), vb. TiN, TiC ve di\u011fer malzemeler gibi diren\u00e7li metal bile\u015fikleri. Y\u00fcksek TiC sertli\u011fi (HV3200), iyi a\u015f\u0131nma direnci, bu nedenle kaplama kal\u0131nl\u0131\u011f\u0131 genellikle 5 ~ 7\u03bcm'dir. D\u00fc\u015f\u00fck TiN sertli\u011fi (HV1800 ~ 2100) substrata d\u00fc\u015f\u00fck bir ba\u011flanma kuvvetine sahiptir, ancak iyi termal iletkenli\u011fe ve y\u00fcksek toklu\u011fa sahiptir. Kaplama kal\u0131nl\u0131\u011f\u0131 8 ~ 12\u03bcm'ye ula\u015fabilir ve substrat\u0131n toklu\u011fu kaplaman\u0131n a\u015f\u0131nma direnci ile birle\u015ftirilebilir. Karb\u00fcr kesici tak\u0131mlar\u0131n genel performans\u0131n\u0131 art\u0131rmak i\u00e7in. Kaplamal\u0131 karb\u00fcr kesici tak\u0131m, iyi a\u015f\u0131nma direnci ve \u0131s\u0131 direncine sahiptir ve \u00f6zellikle y\u00fcksek h\u0131zl\u0131 kesim i\u00e7in uygundur. Y\u00fcksek dayan\u0131kl\u0131l\u0131\u011f\u0131 ve \u00e7ok y\u00f6nl\u00fcl\u00fc\u011f\u00fc nedeniyle, k\u00fc\u00e7\u00fck partilerde ve esnek otomatik i\u015fleme \u00e7e\u015fitlerinde kullan\u0131ld\u0131\u011f\u0131nda tak\u0131m de\u011fi\u015fikliklerinin say\u0131s\u0131n\u0131 azaltmak i\u00e7in kullan\u0131labilir. Zaman, i\u015fleme verimlili\u011fini art\u0131rmak.<\/div>\n
Kaplamal\u0131 \u00e7imentolu karb\u00fcr tak\u0131mlar\u0131, i\u015fleme s\u00fcrecinin otomatik kontrol\u00fcne elveri\u015fli, g\u00fc\u00e7l\u00fc anti-krater a\u015f\u0131nma kabiliyeti, sabit b\u0131\u00e7ak \u015fekli ve oluk \u015fekli, tala\u015f k\u0131rma etkisi ve di\u011fer kesme performans\u0131na sahiptir. Kaplamal\u0131 semente karb\u00fcr kesici tak\u0131m\u0131n alt katman\u0131n\u0131n pasifle\u015ftirilmesi ve iyile\u015ftirilmesinden sonra, boyutsal do\u011fruluk y\u00fcksektir, bu da tak\u0131m de\u011fi\u015fiminin konumland\u0131rma do\u011frulu\u011funa otomatik i\u015fleme gereksinimlerini kar\u015f\u0131layabilir. Yukar\u0131daki \u00f6zellikler, kaplamal\u0131 semente karb\u00fcr tak\u0131mlar\u0131n\u0131n \u00f6zellikle FMS (Esnek \u0130malat Sistemi), CIMS (Bilgisayarla B\u00fct\u00fcnle\u015fik \u0130malat Sistemi) gibi otomatik i\u015fleme ekipmanlar\u0131 i\u00e7in uygun oldu\u011funu belirler. Bununla birlikte, kaplama y\u00f6ntemlerinin kullan\u0131m\u0131, \u00e7imentolu karb\u00fcr matris malzemelerinin zay\u0131f tokluk ve darbe direnci problemini hala \u00e7\u00f6zememektedir. Di\u015fleri g\u00f6rmek i\u00e7in TiN kapl\u0131 karb\u00fcr testere b\u0131\u00e7aklar\u0131 kullan\u0131ld\u0131\u011f\u0131nda, testere di\u015flerinin t\u0131rm\u0131k y\u00fcz\u00fcn\u00fcn a\u015f\u0131nma performans\u0131n\u0131n iyile\u015ftirildi\u011fi bulunmu\u015ftur.<\/div>\n
PVD kapl\u0131 ah\u015fap testere kesme testi, TiN kapl\u0131 WC sert ala\u015f\u0131ml\u0131 testere b\u0131\u00e7a\u011f\u0131 (\u00f6n kaplama di\u015f y\u00fczeyi) sert sunta testereyi testereledi\u011finde testere di\u015fi a\u015f\u0131nma miktar\u0131n\u0131n azald\u0131\u011f\u0131n\u0131 kan\u0131tlar. Bununla birlikte, CVD kaplaman\u0131n daha y\u00fcksek s\u0131cakl\u0131\u011f\u0131, alt-tabaka ve kaplama aras\u0131nda k\u0131r\u0131lgan bir ba\u011flay\u0131c\u0131 faz\u0131n olu\u015fmas\u0131 ile sonu\u00e7lanmaktad\u0131r.<\/div>\n
Kesme kenar\u0131 \u00fczerindeki kaplama, kaplaman\u0131n art\u0131k gerilimi, kesme \u0131s\u0131s\u0131 ve kesme kuvvetinin etkisi alt\u0131nda h\u0131zla soyulur. CVD y\u00f6ntemi ile kar\u015f\u0131la\u015ft\u0131r\u0131ld\u0131\u011f\u0131nda, PVD kaplama s\u0131cakl\u0131\u011f\u0131 d\u00fc\u015f\u00fckt\u00fcr, bu nedenle PVD kaplama arac\u0131 daha iyi bir kaplama yap\u0131s\u0131 ve y\u00fcksek kaplama sertli\u011fi elde edebilir, tak\u0131m kenar\u0131 keskinli\u011fi de geli\u015ftirilmi\u015ftir. Ayr\u0131ca, PVD kaplamal\u0131 tak\u0131mlar daha iyi \u00e7atlama direncine sahiptir. 1990'lar\u0131n ortalar\u0131ndan sonra, ara\u015ft\u0131rmac\u0131lar PVD kaplamal\u0131 karb\u00fcr a\u011fa\u00e7 i\u015fleme aletleri i\u00e7in karb\u00fcr boyutu, ba\u011flay\u0131c\u0131 i\u00e7eri\u011fi ve kaplama malzemeleri \u00fczerinde ara\u015ft\u0131rmalar yapt\u0131lar.<\/div>\n
Karb\u00fcr par\u00e7ac\u0131k boyutu s\u0131ras\u0131yla 0.8, 1.2, 1.5 ve 1.7 um'dir. Kar\u015f\u0131l\u0131k gelen kobalt i\u00e7erikleri s\u0131ras\u0131yla 3%, 4%, 6% ve 10% idi; kaplama malzemeleri s\u0131ras\u0131yla TiN, TiN-Ti (C, N) -TiN idi. TiAlN 2'ye kar\u015f\u0131l\u0131k gelen kaplaman\u0131n kal\u0131nl\u0131\u011f\u0131, aletin t\u0131rm\u0131k y\u00fcz\u00fcne uygulanan s\u0131ras\u0131yla 3.5 um, 5.5 um ve 3 um'dir. Sonu\u00e7lar, kaplaman\u0131n \u00fc\u00e7 kaplama malzemesinin hepsinde soyuldu\u011funu, ancak TiN ve Ti'nin (N, C, N) TiAlN2'den \u00e7ok daha hafif oldu\u011funu ve aletin ince par\u00e7ac\u0131klar ve d\u00fc\u015f\u00fck kobalt i\u00e7erikli a\u015f\u0131nma direncinin 10% artt\u0131\u011f\u0131n\u0131 g\u00f6sterdi. ~ 30%, ancak tak\u0131m kaplamas\u0131n\u0131n y\u00fcksek kobalt i\u00e7eri\u011fi a\u015f\u0131nma direncini azalt\u0131r. \u00c7al\u0131\u015fma ayr\u0131ca, kaplama d\u00f6k\u00fclmesinin temel nedeni d\u00fc\u015f\u00fck kaplama yap\u0131\u015fmas\u0131n\u0131n da oldu\u011funa i\u015faret etti. Kesme ko\u015fullar\u0131nda 2 kat daha uzun tak\u0131m \u00f6mr\u00fc. Kaplamada, kaplaman\u0131n y\u00fczey kaplamas\u0131, taneli ar\u0131tma teknolojisi ile geli\u015ftirilir, b\u00f6ylece kaplama y\u00fczeyi p\u00fcr\u00fczs\u00fczd\u00fcr, b\u00f6ylece kaplanm\u0131\u015f aletin s\u00fcrt\u00fcnmeye kar\u015f\u0131 koyma ve yap\u0131\u015fmaya kar\u015f\u0131 direnme kabiliyetini geli\u015ftirmek de kaplaman\u0131n bir geli\u015fme y\u00f6n\u00fcd\u00fcr. teknolojisi. Tokluk ve a\u015f\u0131nma direnci, titanyum bile\u015fikleri tabakas\u0131n\u0131n d\u0131\u015f y\u00fczeyi, kaplama y\u00fczeyi p\u00fcr\u00fczs\u00fczd\u00fcr, yan y\u00fczey, tak\u0131m a\u015f\u0131nmas\u0131n\u0131n stabilitesini sa\u011flamak i\u00e7in ultra p\u00fcr\u00fczs\u00fcz bir kaplamad\u0131r. Elmas son derece y\u00fcksek sertli\u011fe ve m\u00fckemmel kimyasal stabiliteye sahiptir. A\u015f\u0131nma direnci \u00e7imentolu karb\u00fcr\u00fcn 100 ila 250 kat\u0131d\u0131r. Ayr\u0131ca g\u00fc\u00e7l\u00fc asitlere ve alkalilere direnme kabiliyetine sahiptir, ancak toklu\u011fu \u00e7ok zay\u0131ft\u0131r. Daha sert alet malzemesi alt tabaka olarak kullan\u0131l\u0131yorsa, aletin sadece belirli bir mukavemet ve toklu\u011fa sahip olmas\u0131 de\u011fil ayn\u0131 zamanda iyi a\u015f\u0131nma direnci ve kesime sahip olmas\u0131 i\u00e7in y\u00fcksek sertlik, a\u015f\u0131nma direnci ve kimyasal inertlik tabakas\u0131 uygulay\u0131n. Performans, ah\u015fap i\u015fleme tak\u0131m\u0131n\u0131n a\u015f\u0131nma \u00f6zelliklerini kar\u015f\u0131lamak i\u00e7in, elmas kaplama a\u015f\u0131nmaya kar\u015f\u0131 ideal bir ara\u00e7t\u0131r.<\/div>\n
1950'lerde, y\u00fcksek s\u0131cakl\u0131k ve y\u00fcksek bas\u0131n\u00e7l\u0131 sentetik elmaslar geli\u015ftirilirken, d\u00fc\u015f\u00fck bas\u0131n\u00e7l\u0131 gaz faz\u0131 sentetik elmaslar da ara\u015ft\u0131r\u0131ld\u0131, ancak birikme oran\u0131 yava\u015ft\u0131. D\u00fc\u015f\u00fck bas\u0131n\u00e7l\u0131 gaz faz\u0131 sentetik elmaslar, elmas\u0131n metastabil b\u00f6lgesinde ve grafit faz\u0131n\u0131n kararl\u0131 faz\u0131nda \u00fcretildi. Grafit ve amorf karbon kolayca \u00e7\u00f6keltilir. Bu nedenle, grafit ve amorf karbon olu\u015fumunun ve uzakla\u015ft\u0131r\u0131lmas\u0131n\u0131n engellenmesi, buharla biriken elmas filmlerin anahtar\u0131d\u0131r. 1980'lerin sonunda, maliyetleri azaltmak ve end\u00fcstriyel \u00fcretime ula\u015fmak i\u00e7in, DC plazma jetleri gibi y\u00fcksek h\u0131zl\u0131 biriktirme y\u00f6ntemleri elmas film biriktirme i\u00e7in en h\u0131zl\u0131 b\u00fcy\u00fcyen y\u00f6ntem haline gelmi\u015ftir. Kesme y\u00fczeyi (20 um kaplama kal\u0131nl\u0131\u011f\u0131) olan CVD elmas film kapl\u0131 karb\u00fcr u\u00e7lar kullan\u0131larak yonga levhalar \u00fczerinde yap\u0131lan deneyler, kaplaman\u0131n par\u00e7alanmas\u0131n\u0131n \u00f6l\u00fcmc\u00fcl bir dezavantaj oldu\u011funu g\u00f6stermi\u015ftir. Kaplama soyulmad\u0131\u011f\u0131 s\u00fcrece aletin a\u015f\u0131nmas\u0131 neredeyse hi\u00e7 de\u011fi\u015fmez ve 40 ila 50 \u03bcm'de tutulur. Elmas kaplamal\u0131 karb\u00fcr indeksleme u\u00e7lar\u0131 ile MDF \u00fczerindeki frezeleme testleri, elmas filmlerin farkl\u0131 soyma derecelerine sahip oldu\u011funu g\u00f6sterdi, ancak soyulmam\u0131\u015f film bir "banka" korumas\u0131 oynad\u0131 ve matris malzemesinin a\u015f\u0131nmas\u0131n\u0131 azaltt\u0131, b\u00f6ylece ara\u00e7 A\u015f\u0131nma direnci neredeyse artt\u0131 1 kez. Kaplama i\u015fleminin ve ekipman\u0131n\u0131n iyile\u015ftirilmesi ile, elmas film ile alt-tabaka aras\u0131ndaki ba\u011flanma kuvveti daha da artar ve filmin soyulmas\u0131 kontrol edilir. G\u00fcn\u00fcm\u00fczde, takviyeli zeminin y\u00fczeyinde Al203 a\u015f\u0131nmaya dayan\u0131kl\u0131 tabakay\u0131 kesmek i\u00e7in kullan\u0131lan zemini g\u00fc\u00e7lendirmek i\u00e7in aletler \u00fcretmek i\u00e7in elmas kapl\u0131 \u00e7imentolu karb\u00fcr malzemeler kullan\u0131lm\u0131\u015ft\u0131r. Bununla birlikte, CVD elmas polikristalin filmin safl\u0131\u011f\u0131 \u00e7ok y\u00fcksektir, sertlik (HV9000 ~ 10000) do\u011fal elmas\u0131nkine yak\u0131nd\u0131r ve i\u015flenebilirli\u011fi \u00e7ok zay\u0131ft\u0131r ve geleneksel i\u015fleme veya elektro korozyon ile i\u015flenmesi zordur. Bu nedenle, elmas kapl\u0131 sert ala\u015f\u0131ml\u0131 malzeme, yeniden ta\u015flamayan indeksleme b\u0131\u00e7aklar\u0131n\u0131n \u00fcretimi i\u00e7in uygundur.<\/div>\n
2000'den sonra, elmas CVD kaplamal\u0131 tak\u0131mlar\u0131n performans\u0131 daha da geli\u015ftirilmi\u015ftir. \u00dcr\u00fcnler de\u011fi\u015ftirilebilir ve sert karb\u00fcr tak\u0131mlar\u0131 kapsamaktad\u0131r.<\/div>\n

4. Sonu\u00e7<\/h2>\n
Karb\u00fcr kesici tak\u0131m malzemeleri, mevcut ah\u015fap i\u015fleme end\u00fcstrisinde ana kesici tak\u0131m malzemeleri haline gelmi\u015ftir ve gelecekte ah\u015fap kesme ve i\u015flemede \u00f6nemli bir yer tutacakt\u0131r. \u00c7e\u015fitli sert ala\u015f\u0131m performans\u0131 iyile\u015ftirme teknolojilerinin ve kaplama teknolojilerinin s\u00fcrekli iyile\u015ftirilmesiyle, karb\u00fcr kesici tak\u0131m malzemelerinin kesme performans\u0131 artmaya devam edecek ve ah\u015fap i\u015fleme end\u00fcstrisi ah\u015fap ve ah\u015fap kompozit malzemelerin kesme \u00f6zelliklerinde \u00e7e\u015fitli de\u011fi\u015fiklikler uygulayacakt\u0131r. Kaplama teknolojisi yeni malzemeler elde eder ve sert ala\u015f\u0131ml\u0131 ve sert ala\u015f\u0131ml\u0131 tak\u0131mlar, karb\u00fcr kesme tak\u0131mlar\u0131n\u0131n kesme performans\u0131n\u0131, \u00fcr\u00fcn kalitesini ve \u00fcretim verimlili\u011fini en \u00fcst d\u00fczeye \u00e7\u0131karmak i\u00e7in makul \u015fekilde se\u00e7ilir.<\/div>\n
Bizim tungsten karb\u00fcr ah\u015fap i\u015fleme aletleri<\/a><\/div>\n<\/div>\n<\/div>\n

<\/p>","protected":false},"excerpt":{"rendered":"

Machining is one of the most basic, widest and most important processes in the wood industry, directly affecting production efficiency, processing costs and energy consumption. With the advancement of the wood industry technology, various wood composite materials, plywood, wood, bamboo glulam, especially melamine impregnated paper plywood, PVC plywood, Al 2 O 3 reinforced plywood and…<\/p>","protected":false},"author":1,"featured_media":2813,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"_jetpack_memberships_contains_paid_content":false,"footnotes":""},"categories":[79],"tags":[],"class_list":["post-1845","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-materials-weekly"],"jetpack_featured_media_url":"https:\/\/www.meetyoucarbide.com\/wp-content\/uploads\/2019\/05\/141d2f_4fb30763ef8c4f7fa8c3bef42fb57140mv2-1.jpg","jetpack_sharing_enabled":true,"_links":{"self":[{"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/posts\/1845","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/comments?post=1845"}],"version-history":[{"count":0,"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/posts\/1845\/revisions"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/media\/2813"}],"wp:attachment":[{"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/media?parent=1845"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/categories?post=1845"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/www.meetyoucarbide.com\/tr\/wp-json\/wp\/v2\/tags?post=1845"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}