WC-Co carbide end mills are commonly used for titanium alloy milling. The material characteristics of the tools directly affect the tool life and milling efficiency. Extending the tool life of titanium alloy processing and improving the processing efficiency have always been hot topics in the industry.

In this study, two different high-temperature performance matrix body?materials were prepared by adding trace amounts of TaC (NbC) carbide to the carbide?matrix body. The high-temperature hardness and high-temperature fracture toughness of the two carbides were tested using a high-temperature Vickers hardness tester. Whole carbide?end mills?with the same geometric parameters were prepared based on the two matrix body?materials, and titanium alloy TC4 milling?tests were carried out. By analyzing the tool life and wear patterns, the impact of TaC (NbC) on the wear performance of carbide?milling?tools in high-speed milling was studied.

 

Experimental conditions and testing methods

Two different WC-Co-based carbide?materials with different compositions, named A and B, were prepared for the experiment. Trace amounts of TaC (NbC) carbide were added to material A, with a mass fraction of less than 0.1%. The compositions of the two carbides are shown in Table 1.

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 2

The high-temperature hardness and high-temperature fracture toughness of materials A and B at different temperatures are shown in Figures 2 and 3, respectively.

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 3

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 4

Based on the two carbide?materials A and B, four-flute flat end mills?A and B with the same geometric parameters were prepared accordingly. The specifications and parameters of the tools are shown in Table 2.

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 5

The workpiece material for the milling?test is annealed titanium alloy TC4, with a material hardness of 28.2 HRC. The milling?test was performed on a Mazak Nexus 430A-II vertical machining center, and the machining parameters are shown in Table 3.

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 6

Experimental results and discussion

Under the same milling?conditions, the flank wear curves of end mills?A and B in the machining of titanium alloy TC4 are shown in Figure 4. Figure 5 shows the flank wear morphologies of the two end mills.

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 7

end mills wear

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 8
Fig.5 wear morphology figures of two tools

 

From Figures 4 and 5, it can be seen that when the milling?distance is less than 60m, both types of carbide?end mills?are in the normal wear stage, and the amount of wear on the tool’s back surface increases slowly. This stage is mainly in the early stage of milling, where the tool coating has good wear resistance and insulation, which effectively protects the tool matrix body?during this stage.

However, due to the very high milling?temperature of titanium alloy, as milling?continues, the coating on the tool edge is worn off, exposing the tool matrix body. The tool edge directly bears severe thermal and mechanical shock. As the matrix body?of end mills?A is added with trace alloy carbide TaC (NbC), its high-temperature hardness and high-temperature fracture toughness are higher than that of end mills?B. Therefore, end mills?A has more advantages than end mills?B in terms of the amount of wear on the back surface of the tool.

 

Analysis of end mills failure

After milling?200m using vertical milling cutters A and B, the worn positions of the tool tips were analyzed using a scanning electron microscope. The tip wear morphologies of the two vertical milling cutters are shown in Figure 6.

What are the 3 Points of Influence?will TaC (NbC) Have on the Wear of Carbide?End Mills? 9

From Figure 6, it can be seen that the addition of trace amounts of alloy carbide TaC(NbC) in vertical milling cutter A has improved the high-temperature fracture toughness of the WC-Co carbide, suppressed the formation and propagation of cracks within the tool matrix body, and extended the tool life. On the other hand, the high-temperature fracture toughness of vertical milling cutter B is lower than that of A, and when the milling?edge is subjected to severe thermal shock and mechanical loads, cracks are easily formed and continuously expanded, causing the tool matrix body?material at the milling?edge to break and ultimately resulting in tool failure.

Вывод

Under the same main elements, the carbide?material A with trace amounts of alloy carbide TaC(NbC) has higher high-temperature hardness and fracture toughness than the carbide?material B without adding trace amounts of alloy carbide TaC(NbC). At 800℃, the high-temperature hardness is increased by approximately 14.5%, and the high-temperature fracture toughness is increased by approximately 10.2%.

When milling?titanium alloy TC4 under the same conditions, the tool with added trace amounts of alloy carbide TaC(NbC) has better wear resistance. When the milling?distance is 200m, the amount of wear on the back surface of vertical milling cutter A is 0.076mm, while the amount of wear on the back surface of vertical milling cutter B is 0.13mm.

The high-temperature fracture toughness of the carbide?material A with TaC(NbC) added is better. Under the same milling?conditions, the milling?edge retention of vertical milling cutter A is better, and there are significantly fewer cracks in the worn failure area compared to vertical milling cutter B.

Добавить комментарий

Ваш адрес email не будет опубликован. Обязательные поля помечены *

大鸡巴抽插小穴色虐视频| 国产亚洲精品一区久久| 中文字幕一区二区日韩精品蜜臂| 午夜性无码视频在线播放| 亚洲卡通动漫第127页| 男插女下面高潮视频| 丁香婷婷亚洲六月综合色| 国产成人无码AV一区二区三区| 国产亚洲欧美中文日韩| 日韩人妻无码中字一区二区| 操逼操的翻白眼视频| 欧美日韩视频在线一区二区| 亚洲av 又黄又爽十大| 亚洲国产成人手机版| 猛哥操女人B视频| 美女呻吟翘臀后进爆白浆| 精品精品视频国产| 啊灬啊别停灬用力啊男男在线观看| 操我好舒服用力视频| 国产成人无码AV一区二区三区| 久久久久精品无码专区喝奶| 亚洲 欧美 精品 高清| 精品无码国产一区二区三区A| 大鸡吧天天草黑逼| 骚逼少妇被巨根爆插| 免费看黑人操逼视频| 美国业余自由摘花管| 鸡巴插进女人的逼里| 欧美一区二区三区久久国产精品| 熟妇人妻无乱码中文字幕| 国产精品亚洲综合av| 日本免费暖暖在线小视频| 国产精品熟女视频播放| 九九视频免费在线观看| 国产高清乱码女大生AV| 夫妻性生活在线免费视频| 中文字幕你懂的av一区二区| 免费观看的黄视频一级国产| 国产大码丝袜老熟女av| 插我舔内射18免费视频| 亚洲AV无码一区二区三区天堂古|