Since the first commercial scanning electron microscope came out in 1965, after 40 years of continuous improvement, the resolution of scanning electron microscopy has increased from 25 nm of the first one to 0.01 nm. Most scanning electron microscopy can be combined with X-ray spectrometer and X-ray energy spectrometer, which has become a comprehensive analysis of the surface micro-world. Multifunctional electron microscopy instrument. Scanning electron microscopy (SEM) has become a powerful tool widely used in various scientific fields and industrial sectors. Scanning electron microscopy (SEM) has been widely used in many fields, such as geology, biology, medicine, metallurgy, mechanical processing, materials, semiconductor manufacturing and ceramics inspection.

Scanning electron microscopy (SEM) plays an extremely important role in the field of materials. It is widely used in the study of morphology, interface condition, damage mechanism and material performance prediction of various materials. Scanning electron microscopy (SEM) can be used to study crystal defects and their production process directly. It can observe the aggregation mode of atoms in metal materials and their true boundaries. It can also observe the movement mode of boundaries under different conditions. It can also check the damage and radiation damage caused by crystal in surface machining.

Working Principle of Scanning Electron Microscope

Application of Scanning Electron Microscope in Material Analysis 2

The working principle of the scanning electron microscope is shown in

Fig. 1 Scanning electron microscope schematic diagram

The scanning electron microscope (SEM) is composed of electron beams emitted from an electron gun. Under the action of accelerated voltage, the electron beams converge through a magnetic lens system to form an electronic optical system with a diameter of 5 nm. After two or three electromagnetic lenses, the electron beams converge into a thin electron beam focusing on the surface of the sample. A scanning coil is mounted on the upper side of the final lens, under which the electron beam is scanned on the surface of the sample. Due to the interaction between high energy electron beams and sample materials, various kinds of information are generated: secondary electrons, back-reflection electrons, absorption electrons, X-ray, Auger electrons, cathodoluminescence and transmission electrons. These signals are received by the corresponding receiver, amplified and sent to the gate of the picture tube to modulate the brightness of the picture tube. Because the current on the scanning coil corresponds to the brightness of the picture tube, that is to say, when the electron beam strikes a point on the sample, a bright spot appears on the screen of the picture tube. In this way, scanning electron microscopy (SEM) uses point-by-point imaging method to convert the different features of the sample surface into video signals proportionally in order to complete a frame of images, so that we can observe various characteristic images of the sample surface on the fluorescent screen.

Annex of Scanning Electron Microscope

Scanning electron microscopy (SEM) is usually equipped with a spectrometer or an energy spectrometer. The spectrometer uses Bragg equation 2dsin (= () to excite X-rays from the sample and to separate them by appropriate crystals. The characteristic X-rays with different wavelengths will have different diffraction angles of 2 ().  Spectrometer is a powerful tool for micro-area component analysis. The wavelength resolution of the spectrometer is very high, but its application range is limited because of the low utilization of X-ray. Energy spectrometer is a method of element analysis based on the energy difference of X-ray quantum. For an element, when the X-ray quantum transits from the main quantum number stomach N1 to the main quantum number n2, there is a specific energy (=(n1-(n2). Energy dispersive spectrometer has high resolution and fast analysis speed, but its resolution ability is poor. There are often overlapping lines, and the accuracy of element analysis for low content is very poor.

Spectrometers and energy spectrometers can not replace each other, but complement each other.

Application of Scanning Electron Microscope in Material Science

Observation of Surface Morphology of Materials

Application of Scanning Electron Microscope in Material Analysis 3

FIGURE 1 SEM MORPHOLOGY OF HOT ROLLED Mg SIDE PEELLING SURFACE

The SEM morphology of Mg side peeling surface of hot rolled Al-Mg clad sheet (rolling temperature 400 C, reduction rate 45%) is shown in Figure 1. From the graph, we can clearly see that there are a lot of tearing edges and platforms on the peeling surface, and there are many small radial stripes and dimples on the tearing platform.

Second Phase of Observing Material

Application of Scanning Electron Microscope in Material Analysis 4

Figure 2 High-power Microstructure of AZ31 Magnesium Alloy by SEM

It can be clearly seen from Fig. 2 that the size of the second phase Mg17Al12 after fragmentation is about 4 m, and there are many dispersed small particles near the “bulk” Mg17Al12 with the size of about 0.5 m. This is the second phase Mg17Al12 precipitated from the supersaturated solid solution of a-Mg base during the cooling process after hot rolling, showing the fineness of this morphological distribution. Biphasic Mg17Al12 can effectively inhibit dislocation movement, improve material strength and play the role of dispersion strengthening, but will not significantly reduce the plasticity of AZ31 magnesium alloy.

Observation of Material Interface

Application of Scanning Electron Microscope in Material Analysis 5

Figure 3 Mg/Al rolling interface line scanning [1]

Fig. 3 is a line scan image of Mg/Al rolling composite interface. From the graph, we can see that the line scan through the interface between Mg and Al can be obtained. On the Al side, the Mg content is low, and on the Mg side, Al is almost zero. However, at the interface, about half of Mg and Al occur, indicating that the diffusion occurs at the interface, forming Mg and Al. Diffusion layer.

Observation of material fracture

材料分析における走査型電子顕微鏡の応用6

(a) As-cast  

Application of Scanning Electron Microscope in Material Analysis 7

 (b) Hot-rolled

Figure 4 Tensile Fracture Morphology of AZ31 Magnesium Alloy

The SEM scanning morphology of tensile fracture of as-cast AZ31 magnesium alloy is shown in Fig. 3-6. From Fig. 4 (a), it can be seen that there are obvious cleavage fracture platforms and a few dimples at the final tear point, which are basically quasi-cleavage fracture with poor plasticity. This is because there is a large brittle second phase Mg17Al12 at the grain boundary of as-cast AZ31 magnesium alloy, which is easy to crack and form crack source during tensile deformation. The fracture morphology of hot rolled AZ31 magnesium alloy shows obvious necking phenomenon. As shown in Figure 4 (b), the macro fracture morphology of AZ31 magnesium alloy shows ductile fracture morphology with dimple size ranging from 5 to 20 m.

おわりに

Scanning electron microscopy (SEM) is widely used in material science. It can be used not only in the above aspects of material science, but also in fatigue failure of metals and morphological observation of impurities. As a student majoring in materials, we should understand the working principle and application of scanning electron microscopy, and make full use of the tool of scanning electron microscopy in our scientific research to conduct a comprehensive and meticulous study of materials.

精品美女久久久久久嘘嘘| 国产合区在线一区二区三区| 国产高清在线观看一区二区三区| 97性无码区免费| 瓯美在线免费视频笫一区第二区| 国产高清在线观看一区二区三区| 亚洲成国产人片在线观看| 潮中文字幕在线观看| 搞段B片黄色全免费看看| 亚洲国产成久久成人综合一区| 97人妻精品一区二区三区视频| 国产高清在线观看一区二区三区| 久久国产精品二卡| 狂野国产性爱av| 中文字幕乱码人妻一区二区三区| 美女被大屌操大骚逼| 日本入室强伦姧人妻中文| 亚洲午夜福利视频在线| 中文字幕一区二区三区中文字幕| 一级做a爱过程免费视频俩| 男人把昆吧放女人屁股里| 欧美黑屌操B内射冒白浆| 欧美精品一区二区三区四区五区| 日韩美女在线视频一区不卡| 激情五月六月婷婷俺来也| 亚洲一区二区女同性恋免费看| 啊好爽好多水深插射视频| 女人扒开腿让我舔十八禁| 日本中文字幕无人区一区二区| 三级片成人京东热五月天| 日韩视频无码日韩视频又2020| 无码中文字幕免费一区二区三区| 一区亚洲免费二区| 操烂嫩逼内射视频| 中日韩中文字幕无码一本| 这里只有久久精品| 中文字幕一高清免费视频| 色欲色欲色视频综合| 日韩精品无码一区二区三区不卡| 99久久九九爱精品国产| 91啪国线自产2019|